TEGOMER® M-Si 2650 is an organo-modified siloxane containing non-reactive aromatic groups. TEGOMER® M-Si 2650 improves the processing and the performance of polyolefins, engineering resins, thermoplastic elastomers and silicon rubber.
Typical Applications
TEGOMER® M-Si 2650 is used as an additive for
TEGOMER® M-Si 2650 improves the rheological properties during processing, e.g. compounding, extrusion and moulding of parts based on the above-mentioned systems.TEGOMER® M-Si 2650 improves the surface characteristics of the final parts, e.g. the appearance of resin / fibre mixes.
- Thermoplastic elastomers, e.g. TPE-V or TPE-S
- Engineering resins such as PS, PBT, PA
- Polyolefins
- Silicone elastomers
TEGOMER® M-Si 2650 improves the rheological properties during processing, e.g. compounding, extrusion and moulding of parts based on the above-mentioned systems.TEGOMER® M-Si 2650 improves the surface characteristics of the final parts, e.g. the appearance of resin / fibre mixes.
Benefits at a glance
- Easier processing
- Higher through-put rates
- Improved mould release properties for injection moulding especially relevant for tacky or low shore hardness elastomers
- Higher surface quality giving better scratch, abrasion and wear resistance, e.g. PMMA & PA
- Reduction of COF in all polymers
- Enhanced hydrophobicity / lower water uptake, e.g. for polyamide
- Reduced tackiness in silicone rubber especially HCR resulting in lower dirt pick up
- Enhancement of flame resistance, e.g. in PA and PBT using phosphorus-based flame retardants